In addition, hyaluronic acid, chondroitin sulfate and similar salts, aluminum zirconium glycine complex, and neutralized salts of acid-alkali as used in cosmetic formulation may be used. A film of this silicone resin had a refractive index of 1.488. The phenylsilicone resin should have a weight average molecular weight (Mw) of 1,000 to 8,000, preferably 2,000 to 7,000, more preferably 2,000 to 6,000. Embodiment II of the invention is a method for preparing the silicone resin, comprising the following steps. A wrinkle concealer was prepared by step A of mixing ingredients 1 to 6 until uniform. Examples include inorganic powders, organic powders, surface active metal salt powders, color pigments, pearly pigments, metal powder pigments, tar dyes, and natural dyes. From shop kathyfinton . A powder foundation was prepared by step A of grinding and mixing ingredients 1 to 8 until uniform, step B of mixing ingredients 9 to 12 until uniform, step C of adding B to A and mixing until uniform, and step D of press molding C in a mold. A mascara was prepared by step A of adding ingredients 7 and 13 to ingredient 9 and mixing the contents uniformly while heating, step B of adding ingredients 1 to 6 and 8 to A and mixing the contents uniformly, step C of adding ingredients 10, 11 and 12 to B, and uniformly dispersing the contents on a roller. At the end of dropwise addition, the solution was heated at 40-60° C. for 5 hours to conduct hydrolytic condensation reaction, yielding a silicone resin solution. Privacy Policy The skin-friendly, hydrophobic, acid and alkali resistance characteristics of silicone products, as well as the excellent film-forming properties of specific silicone products, make silicone products widely used in personal care and cosmetics industries. siliconeoil. Patent Document 6: JP-A 2009-019033 (U.S. Pat. Suitable UV absorbing/scattering agents include microparticulate titanium oxide, microparticulate iron-containing titanium oxide, microparticulate zinc oxide, microparticulate cerium oxide, and composites thereof, and UV absorbing/scattering powders. A film-forming agent may be added to the cosmetic composition. The silicone resin of Comparative Example 1 was a high viscosity liquid. Samples are marked based on the average of each evaluation item, with the results shown in Table 8. The solution was heated at 100° C. for 3 hours, then at 130° C. for 2 hours to remove the ethanol formed and excess of water, after which it was cooled. As long as the benefits of the invention are not compromised, optional ingredients other than the phenylsilicone resin may be used alone or in combination and in any suitable amounts in the cosmetic composition. Next, 3.5 g of 25% sodium hydroxide aqueous solution and 0.5 g of calcium carbonate were added to the solution to neutralize the acid, after which 22 g of triphenylsilanol and 300 g of isododecane were added to the solution. This was followed by distillation in vacuum, controlled dilution with isododecane to a silicone resin concentration of 50%, and filtration, yielding a 50% isododecane solution of a silicone resin having a Mw of 3,500 and consisting of (C6H5)3SiO1/2 units, (CH3)3SiO1/2 units, (C6H5)2SiO2/2 units, (C6H5)SiO3/2 units and SiO4/2 units in a molar ratio of 0.07:0.33:0.06:0.11:0.43. MakingCosmetics - Silicone Resin - 8.8oz / 250g - Cosmetic Ingredient: Amazon.ca: Beauty. We have a variety of silicone resin molds for all types of designs and sizes. Says senior scientist for Cover Girl Sarah Vickery, who is based in Hunt Valley, Md., ‘Silicones are critical in many foundation formulations to give them more ‘spreadability’ and a luxurious, comfortable feel on skin. Herein R1 is a group, exclusive of phenyl, selected from among C1-C8 alkyl groups, C6-C12 aryl groups and C1-C8 fluorinated alkyl groups, R2 and R3 are each independently a group selected from among C1-C8 alkyl groups, C6-C12 aryl groups and C1-C8 fluorinated alkyl groups, a is a number of 0 to 0.2, b is a number of 0.1 to 0.5, c is a number of 0 to 0.2, d is a number of 0.01 to 0.5, e is a number of 0 to 0.6, a+b+c+d+e is equal to 1.0. This was followed by distillation in vacuum, controlled dilution with isododecane to a silicone resin concentration of 50%, and filtration, yielding a 50% isododecane solution of a silicone resin having a Mw of 10,160 and consisting of (CH3)3SiO1/2 units, (C6H5)SiO3a units and SiO4/2 units in a molar ratio of 0.29:0.20:0.51. Get it as soon as Tue, Jan 5. Next, 3.5 g of 25% sodium hydroxide aqueous solution and 0.5 g of calcium carbonate were added to the solution to neutralize the acid, after which 1.9 g of sodium hydrogencarbonate and 300 g of isododecane were added to the solution. Since the silicone resin did not dissolve in isododecane, the liquid was white turbid and could not be filtered. It is noted that the silicone resin prior to filtration had a Mw of 4,310 and consisted of (CH3)3SiO1/2 units and (C6H5)SiO3/2 units in a molar ratio of 0.25:0.75. After the dropwise addition of water, hydrolytic condensation reaction is continued preferably while heating at 30 to 100° C., especially 50 to 80° C. for 2 to 8 hours. This was followed by distillation in vacuum, controlled dilution with isododecane to a silicone resin concentration of 50%, and filtration, yielding a 50% isododecane solution of a silicone resin having a Mw of 2,950 and consisting of (C6H5)3SiO1/2 units, (CH3)3SiO1/2 units, (C6H5)SiO3/2 units and SiO4/2 units in a molar ratio of 0.03:0.36:0.33:0.28. A liquid W/O foundation was prepared by step A of mixing part of ingredient 1, ingredients 11 and 12, and part of ingredient 20 and dispersing them uniformly, step B of mixing ingredients 8 to 10 until uniform, step C of mixing remainder of ingredient 1, ingredients 2 to 7, adding B thereto, dispersing and mixing the contents uniformly, step D of mixing ingredients 13 to 18 and remainder of 20 until uniform, and step E of slowly adding ID to C while stirring, emulsifying, and adding A and ingredient 19 thereto. Examples include silicone oils having a low viscosity of 0.65 mm2/sec to 100.0 mm2/sec at 25° C., hydrocarbon oils such as liquid paraffin, squalane, isododecane, and isohexadecane, glyceride oils such as trioctanoin, ester oils such as isotridecyl isononanoate, N-acylglutamic acid esters, and lauroyl sarcosine acid esters, and animal and plant oils such as macadamia nut oil. Silicone resins are recognised for their ability to reduce transfer from colour cosmetics such as lipsticks. Next, 3.5 g of 25% sodium hydroxide aqueous solution and 0.5 g of calcium carbonate were added to the solution to neutralize the acid, after which 22 g of triphenylsilanol, 1.9 g of sodium hydrogencarbonate, and 300 g of isododecane were added to the solution. Nowadays, further improvements in water resistance, sweat resistance and long lasting performance are demanded as well as luster and color development. The inventors have found that a phenylsilicone resin comprising specific constituent units is soluble in oily ingredients such as silicone oils and organic oils, able to form a uniform continuous film free of sticky feel and brittleness, and compatible with UV absorbers, and that a cosmetic composition comprising the phenylsilicone resin offers a pleasant feel on use and eliminates secondary staining or transfer to clothes or the like. The solvent is preferably used in an amount of 5 to 50% by weight of the entire hydrolytic condensation reaction system. In Isododecane silicone resin dissolves the quickest (< 20 min), in cyclomethicone about 20-30min. It is noted that refractive index is measured by removing solvent from a phenylsilicone resin solution to form a film having a thickness of about 1 mm, and analyzing the film at a temperature of 25° C. by means of a refractometer, for example, Abbemat (Anton Paar GmbH). Specifically, R1 is preferably C1-C3 alkyl, with methyl being more preferred. *5 KP-575 by Shin-Etsu Chemical Co., Ltd. Crosslinked alkyl polyether-modified silicone *1, Crosslinked alkyl-modified dimethylpolysiloxane *2. The suntan milky lotion thus obtained was light spreading, non-sticky, and non-oily, and gave a light feeling. A silicone resin represented by the compositional formula (1) and having a weight average molecular weight of 1,000 to 8,000, Click for automatic bibliography Suitable preservatives include alkyl p-hydroxybenzoates, benzoic acid, sodium benzoate, sorbic acid, potassium sorbate, and phenoxyethanol. A transparent cleansing lotion was prepared by step A of mixing ingredients 1 to 4 until uniform, step B of mixing ingredients 5 to 10 until uniform, and step C of slowly adding A to B while stirring, and emulsifying. Suitable UV protective cosmetics include sun cutting or sun care oil, sun cutting milky lotion, sun cutting cream, and sun cutting lotion. When used, the amount of the film-forming agent blended is preferably 0.1 to 20% by weight, more preferably 1 to 10% by weight based on the cosmetic composition. Inter alia, aliphatic alcohols of 1 to 10 carbon atoms are preferred, with ethanol and isopropyl alcohol (IPA) being more preferred. The compounds having formulae (2) to (6) may be used alone or in any desired combination of two or more. The cosmetic composition of any one of 9 to 17, which is a skin care cosmetic, hair care cosmetic, make-up cosmetic, UV care cosmetic or antiperspirant. An O/W cream was prepared by step A of mixing ingredients 1 to 9 while heating, step B of mixing ingredients 10 to 12 and 14 while heating, and step C of slowly adding B to A while stirring, cooling and adding ingredient 13 thereto. Allegedly these compositions form films having water resistance. The subscript b is a positive number of 0.1 to 0.5, preferably 0.2 to 0.45, more preferably 0.2 to 0.4. A method for preparing the silicone resin of 3, comprising the steps of: (i) effecting hydrolytic condensation of at least one organosilicon compound selected from the general formulae (2) and (3): wherein R1 is as defined above with at least one compound selected from silanes having the general formulae (4), (5) and (6): wherein R2 and R3 are as defined above, R4 is each independently hydrogen or a substituted or unsubstituted monovalent hydrocarbon group and partial hydrolytic condensates thereof, in a solventless system or a solvent, and. Suitable anti-inflammatory agents include arantoin, glycyrrhizic acid and salts thereof, glycyrrhetinic acid, stearyl glycyrrhetinate, tranexamic acid and azulene. An average of ratings was calculated. The invention includes embodiment I relating to a phenylsilicone resin, embodiment II relating to a method for preparing the phenylsilicone resin, and embodiment III relating to a cosmetic composition comprising the phenylsilicone resin, which are described below in order. Sponges & Disposables; Makeup Accessories; Brushes; Brush Cleaners; Fun Stuff; Gift Cards; Cosplay Essentials; Education; Silicones, Resins etc . *4 KP-575 by Shin-Etsu Chemical Co., Ltd. *5 treated with AES-3083 by Shin-Etsu Chemical Co., Ltd. *2 KSP-105 by Shin-Etsu Chemical Co., Ltd. *3 SPD-Z6 by Shin-Etsu Chemical Co., Ltd. Alkyl-modified crosslinked polyether-modified. The solution was heated at 100° C. for 3 hours, then at 130° C. for 2 hours to remove the ethanol formed and excess of water, after which it was cooled. The eye liner thus obtained was light spreading, easy to draw eye lines, light feeling, and very long lasting. 14. Buy It Now. Silicones also act as skin protectant, conditioner, pearlizer, film-former, moisturizer, thickener, and emulsifier. Examples of the silicone resin, exclusive of the phenylsilicone resin, include KF-7312J, KF-7312K, KF-7312T, X-21-5249, X-21-5250, KF-9021, X-21-5595, and X-21-5616 from Shin-Etsu Chemical Co., Ltd. IOTA 54 DIPHENYL DIMETHICONE. Brand New. The hand cream thus obtained was non-oily, light feeling, and light spreading and sustained a skin protecting effect.